| 摘要 |
<P>L'INVENTION CONCERNE UN ALLIAGE A BASE DE CUIVRE AYANT UNE RESISTANCE MECANIQUE ET UNE CONDUCTIVITE ELECTRIQUE ELEVEES ET UNE SENSIBILITE A LA TREMPE REDUITE ET SON PROCEDE DE PREPARATION.</P><P>LE PROCEDE DE L'INVENTION COMPREND LES ETAPES SUIVANTES: ON COULE UN ALLIAGE CONSISTANT ESSENTIELLEMENT EN ENVIRON 0,05 A 1,25 EN POIDS DE CHROME, ENVIRON 0,05 A 1,0 EN POIDS DE ZIRCONIUM, ENVIRON 0,01 A 0,15 EN POIDS DE FER ET LE COMPLEMENT ESSENTIELLEMENT DE CUIVRE; ON SOUMET LEDIT ALLIAGE A UN FACONNAGE A CHAUD AVEC UNE TEMPERATURE INITIALE D'ENVIRON 930 A 1000C ET UNE TEMPERATURE DE FINISSAGE SUPERIEURE A ENVIRON 700C; ON TREMPE LEDIT ALLIAGE FACONNE A CHAUD DE LADITE TEMPERATURE DE FINISSAGE A UNE TEMPERATURE INFERIEURE A ENVIRON 300C; ET ON SOUMET LEDIT ALLIAGE A UN RECUIT DE PRECIPITATION A UNE TEMPERATURE D'ENVIRON 350 A 550C PENDANT UNE DUREE DE PLUS D'ENVIRON 30 MIN.</P>
|