<p>Coatings for iron-, nickel- and cobalt-base superalloys. The coatings are applied in order to provide good oxidation/sulfidation and thermal fatigue resistance for the substrates to which the coatings are applied. The coatings consist essentially of, by weight, 10 to 50% chromium, 3 to 15% aluminum, 1.0 to 15% metal mixture from the group consisting of tantalum, tungsten, manganese and combinations thereof, up to 5% reactive metal from the group consisting of lanthanum, yttrium and other rare earth elements, up to 5 percent of rare earth and/or refractory metal oxide particles, and the balance selected from the group consisting of nickel, cobalt and iron, and combinations thereof. Additions of titanium up to 5% and noble metals up to 15% are also contemplated. Tantalum makes up at least 20% of the metal mixture or 0.5% of the total coating weight, whichever is greater. Tungsten, manganese, or a combination thereof, make up at least 0.5% of the total coating.</p> |