| 摘要 |
A metal powder, suitable for magnetic recording, consisting essentially of iron, the individual particles being acicular and containing on average no more then 5 pores and consisting on average of no more than 2 metal cores is produced by precipitating and oxidizing an aqueous iron-(II)-salt solution to produce finely divided acicular iron-(III)-oxide-hydroxide, stabilizing it as by treatment with cadmium, lead, calcium, magnesium, zinc, aluminum, chromium, tungsten, a phosphorus oxide and/or a boron oxide, converting it into ferromagnetic iron oxide of low pore content, and reducing it to metallic iron with a gaseous reducing agent at about 300 DEG to 600 DEG C. |