| 摘要 |
A crosslinked, soft, flexible, closed-cell foam of chlorinated high density polyethylene and a process for the preparation thereof, comprising admixing a high density chlorinated polyethylene with a thermally decomposable chemical foaming agent at a temperature below the decomposition temperature of said foaming agent, molding the chlorinated high density polyethylene into desired form at a temperature below the decomposition temperature of the foaming agent, subjecting the molded chlorinated high density polyethylene to irradiation cross-linking at a temperature below the decomposition temperature of said foaming agent and contacting, in a substantially oxygen-free environment, the crosslinked chlorinated high density polyethylene with a heat transfer medium maintained at a temperature of from about 150 DEG C. to about 350 DEG C. for a period sufficient to form the desired product.
|