L'INVENTION CONCERNE UN PROCEDE DE SYNTHESE DE ZEOLITES4A AYANT UNE CRISTALLINITE ELEVEE ET UNE FINE GRANULOMETRIE, PAR ADDITION, DANS UN PREMIER STADE, D'UNE SOLUTION DE SILICATE DE SODIUM A UNE SOLUTION D'ALUMINATE DE SODIUM (CONTENANT UN EXCES DE NAOH ET CHAUFFEE A UNE TEMPERATURE DE 50 A 100C) ET PAR CRISTALLISATION, DANS UN SECOND STADE, A UNE TEMPERATURE COMPRISE ENTRE 70 ET 105C, CE PROCEDE ETANT CARACTERISE EN CE QUE LA TEMPERATURE DU SILICATE EST INFERIEURE D'AU MOINS 20C A CELLE DE L'ALUMINATE LES RAPPORTS MOLAIRES SIO:HO ET SIO:NAO DANS LA SOLUTION DE SILICATE ETANT RESPECTIVEMENT DE 0,030 A 0,150 ET DE 1,95 A 2,30, ET LE RAPPORT PONDERAL ENTRE LA LIQUEUR-MERE ET LA ZEOLITE AINSI FORMEE ETANT COMPRIS ENTRE 6,5 ET 20.
|