| 摘要 |
This invention is concerned with the production of chemically strengthened polychromatic glasses. In the preferred embodiment, the glasses are suitable for ophthalmic applications, i.e., the glasses have a refractive index of at least 1.523 and, after chemical strengthening, will exhibit a surface compression layer having a depth of at least 0.002'', a maximum central tension of at least 0.7 kg/mm2, and a modulus of rupture of at least approximately 30,000 psi such as to pass the FDA strength requirements for glass ophthalmic lenses. For this preferred embodiment, the chemical strengthening reaction will be conducted for a period not exceeding about 24 hours and the glasses will have compositions consisting essentially, by weight on the oxide basis as calculated from the batch of about 11-18% Na2O, 60-70% SiO2, 3-12% ZrO2, 0-18% ZnO and/or 0-14% Al2O3, the total ZnO+Al2O3 not exceeding about 20%, 0-5% BaO, 0.005-0.3% Ag, 0.01-0.2% CeO2, 1-4% F, and an amount of at least one halide selected from the group of Cl, Br, and I sufficient to react stoichiometrically with the Ag, but not more than about 3%.
|