A method of developing compressive residual stresses in the surface region of a high carbon steel alloy article is disclosed. The article is made of an alloy having 0.8-1.6% C, 0.2-5% Cr, 0-20% ingredients selected from the group consisting of MN, V, Mo, W, Si, and the remainder Fe. The article is heated in a carburizing atmosphere at 800 DEG -950 DEG C. for 1-2.5 hours, and then quenched to cool the central core of the article at a rate sufficiently fast to suppress the formation of non-martensitic austenite decomposition products, thereby establishing a residual compressive stress gradient proceeding from the surface to a depth of 0.007-0.03 inches.
|