| 摘要 |
This invention relates to a heat-resistant composite magnet comprising 2 to 30% by weight of an organic-inorganic compound binder containing boron and silicon and 70 to 98% by weight of the powder of one or more permanent magnets. This invention further relates to a method for producing a heat-resistant composite magnet, which comprises the steps of (a) adding the powder of one or more permanent magnets to a solution of an organic-inorganic compound binder containing boron and silicon dissolved in an organic solvent; (b) evaporating said solvent; (c) molding the resultant permanent magnet powder covered with said binder under a pressure of 0.1 to 5 tons/cm2 in the presence or in the absence of a magnetic field of 12,000-5,000 oersted, the molded product being heated at 200 DEG -450 DEG C. during the molding or after the molding; and (d) cooling the molded product. This invention still further relates to a method for producing a heat-resistant composite magnet, which comprises the steps of (a) molding the powder of one or more permanent magnet at room temperature under a pressure of 0.1 to 5 tons/cm2 in the presence or in the absence of a magnetic field of 12,000-5,000 oersteds; (b) dipping the molded product in a solution of an organic-inorganic compound binder containing boron and silicon; (c) drying the dipped product; (d) heating the dried product at 200 DEG -450 DEG C.; and (e) cooling the heated product. |