| 摘要 |
<P>PROCEDE DE FABRICATION DE DEMI-PRODUITS EN ALLIAGE AL-MN.</P><P>AU DEPART D'UNE MASSE FONDUE COMPORTANT 0,8 A 2 DE MANGANESE, 0,6 A 3 DE SILICIUM, 0,2 A 1 DE FER, 0 A 0,2 DE CUIVRE, 0 A 0,2 DE MAGNESIUM, LE COMPLEMENT ETANT CONSTITUE D'ALUMINIUM ET D'IMPURETES, ON PREPARE UNLINGOT QUI EST RECUIT PENDANT 2 A 20 HEURES A UNE TEMPERATURE DE 400 A 620 C ET QUI EST ENSUITE AMENE PAR DEFORMATION A CHAUD ET A FROID JUSQU'AUX DIMENSIONS FINALES, ET QUI FINALEMENT SUBIT UN RECUIT DE RECRISTALLISATION A PLUS DE 450 C.</P><P>APPLICATION A L'OBTENTION DE PRODUITS SOUDABLES ET EMAILLABLES PRESENTANT DE BONNES PROPRIETES DE CORROSION ET QUI, A L'ETAT TOTALEMENT CRISTALLISE, ONT ENCORE UNE RESISTANCE A LA TRACTION D'AU MOINS 150 NMM.</P>
|