发明名称 |
HIGHLY GRAPHITIZED POROUS CARBON FIBER SHEET AND PRODUCTION THEREOF |
摘要 |
PURPOSE:To improve graphitization degree, chemical resistance and electroconductivity by forming uncalcined organic fiber used as a starting material to sheet and calcining the resultant sheet. CONSTITUTION:A solution of thermosetting resin is impregnated into a fiber aggregate sheet containing an organic fiber for producing uncalcined carbon fiber at an amount of 65wt.% and the impregnated sheet is dried and the surface of the above-mentioned fiber is coated with the above-mentioned thermosetting resin. Then the thermosetting resin is thermally cured to prepare a precursor sheet, which is then subjected to stabilization treatment in oxygen-containing atmosphere at 150-350 deg.C for >=5hr. The precursor sheet after stabilization treatment is calcined in an inert gas atmosphere at >=180 deg.C to provide the highly graphitized porous carbon fiber sheet. |
申请公布号 |
JPH0292881(A) |
申请公布日期 |
1990.04.03 |
申请号 |
JP19880242473 |
申请日期 |
1988.09.29 |
申请人 |
OJI PAPER CO LTD |
发明人 |
IWAKI OSAMU;MIYAMOTO YOSHIHIRO |
分类号 |
C04B38/06;C01B31/02;H01M4/88;H01M4/96 |
主分类号 |
C04B38/06 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|