发明名称 |
METHOD OF PRODUCING IMPROVED METAL ALLOY PRODUCTS |
摘要 |
<p>A dispersion strengthened aluminium alloy sheet is produced by casting an Al-Fe 1.1 - 2.5% alloy, optionally containing Si up to 2.0% and, optionally, proportions of other specified alloying constituents. The alloy is cast in the form of a slab at a growth rate in excess of 25 cms/min. and a thickness of less than 25 mms so that the intermetallics are formed in the slab in the form of fine rods of a diameter of 0.05 - 0.5 microns. These rods are then segmented by reducing the slab by at least 60% by cold-rolling to develop a dispersion of fine intermetallic particles. By final annealing the rolled sheet at a temperature in the range of 250 - 400.degree.C a sheet having a good combination of yield strength and formability is obtained (as indicated by a yield strength of greater than 15 ksi and tensile elongation greater than 15%).</p> |
申请公布号 |
CA1043671(A) |
申请公布日期 |
1978.12.05 |
申请号 |
CA19750239662 |
申请日期 |
1975.11.14 |
申请人 |
ALCAN RESEARCH AND DEVELOPMENT LIMITED |
发明人 |
MORRIS, LARRY R.;THOMSON, JOHN D. |
分类号 |
C22C21/00;B21B3/00;C22C1/02;C22F1/00;C22F1/04;C30B21/02;(IPC1-7):22C21/00;22F1/04 |
主分类号 |
C22C21/00 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|