An improved process for imparting durable flame retardancy to textile materials wherein said material is impregnated with a solution having a poly(hydroxymethyl) phosphonium cation content of from about 10 to about 60 percent by weight, dried to a moisture content of from about 0 to about 8 percent, aerated by passing air through the dried material, cured by polymerizing the monomer on and in the cellulose material with exposure in an enclosed chamber to an atmosphere containing gaseous ammonia and thereafter contacting with water, the improvement comprising, impregnating said material with a poly(hydroxymethyl) phosphonium cation containing solution and a basic catalyst, said solution having a pH of from about 2 to about 9, and after contacting said material with said water, further exposing said material to an atmosphere containing gaseous ammonia.
|