| 摘要 |
A process of melting down and purifying silicon, which comprises melting silicon in at least half of the amount up to double of the amount of a silicate melt heated by resistance heating up to a temperature of at least 1,420 DEG C., said melt consisting of 2-30% by weight of calcium oxide, 5-35% by weight of magnesium oxide, wherein the sum of calcium oxide and magnesium oxide will be 15-38% by weight, 0.5-28% by weight of aluminum oxide and 45-70% by weight of silicon dioxide, and wherein, to the melt are added at least 0.29% by weight of elementary and/or chemically bound copper, preferably 0.50-3% by weight, calculated on the silicon amount. |