| 摘要 |
<p>A hardened cement material having enhanced flexural strength, heat resistance, and water resistance prepared from a cement composition comprising 100 parts by weight of a hydraulic cement material containing gamma -dicalcium silicate ( gamma -C2S) preferably in an amount of 1% by weight or more and 1 to 20 parts by weight of a water-dispersible polymeric material, and mixed with 5 to 25 parts by weight of water, by a molding procedure and by a heat-hardening procedure at a temperature of from 40 DEG C. to 180 DEG C. while controlling the relative humidity to 20% to 70% and/or applying a pressure of 5 to 15 atmospheres.</p> |