Hold and cool process for superalloy joining

摘要

Ni base superalloys containing relatively large amounts of Al and/or Ti are known to be difficult to weld satisfactorily. As the Al and Ti content of the superalloy is increased to improve the strength, the weldability of the component is drastically reduced. It is concluded herein that reducing the γ′ phase improves weldability. A stepwise, controlled heating and cooling process is described to be used in cooperation with a welding process to reduce the γ′ present and thereby improve weldability.

主权项

1. A nickel base superalloy, alloy 247, including a welded seam therein wherein said welded seam was produced by the process of:
a) prior to welding, heating the weld location to an initial predetermined temperature above about 2100 deg. F. with a first heat source, b) welding said nickel base superalloy with a second heat source; and, c) removing said second heat source immediately upon completion of said welding; and, d) performing a controlled step cooling of said weld location such that no more than about 30 weight percent of the γ′ phase is formed at any hold temperature during the step cool and hold process; and, e) cooling said weld location to room temperature to produce a final γ′ weight percent of less than 30 percent.