| 摘要 |
Improved powder coating compositions are disclosed which a particulate mixture of (1) an epoxy-functional copolymer of about 5 to about 20 weight percent of a glycidyl ester of a monoethylenically unsaturated acid and about 95 to about 80 weight percent of monoethylenically unsaturated monomers consisting essentially of monofunctional monomers selected from the group consisting of esters of a C1 - C8 monohydric alcohol and acrylic acid, esters of a C1 - C8 monohydric alcohol and methacrylic acid and C8 - C12 monovinyl hydrocarbons, and having a glass transition temperature in the range of 40 DEG to about 90 DEG C. and a molecular weight (Mn) in the range of about 1,500 to about 15,000, (2) an anhydride crosslinking agent selected from the group consisting of (a) monomeric anhydrides of dicarboxylic acids and (b) homopolymers of monomeric anhydrides of dicarboxylic acids, and present in an amount that provides about 0.3 to about 1.2 anhydride groups for each epoxy group on said copolymer, and (3) a hydroxy carboxylic acid having a melting point in the range of about 400 DEG to about 150 DEG C. and present in an amount such as to provide about 0.1 to about 0.4 carboxyl groups per epoxy group in said copolymer.
|