L'INVENTION CONCERNE UN EMAIL DENTAIRE, CAPABLE DE MATURATION A UNE TEMPERATURE COMPRISE ENTRE 750 ET 850C, C'EST-A-DIRE INFERIEURE D'AU MOINS 90C A LA TEMPERATURE DE VITRIFICATION DE LA PORCELAINE DENTAIRE, ET DONT LA COMPOSITION, EN EN POIDS, EST ESSENTIELLEMENT LA SUIVANTE: SIO 45 A 52, BO 15 A 20, ALO 10 A 15, KO 3,5 A 7,5, NAO 12 A 17, CAO 0 A 1, ZNO 0 A 1, F 1 A 3.CET EMAIL AYANT UNE DIMENSION MOYENNE DE PARTICULES DE 104 MICRONS, ET 1 AU MAXIMUM DES PARTICULES AYANT UN DIAMETRE SUPERIEUR A 30 MICRONS. |