<p>A method is described to prepare a highly textured oxide superconductor article in a single deformation-sinter process. A precursor article including a plurality of filaments comprising a precursor oxide having a dominant amount of a tetragonal BSCCO 2212 phase and a constraining member substantially surrounding each of the filaments is provided. Each of the filaments extends along the length of the article. The oxide article is subjected to a heat treatment at an oxygen partial pressure and temperature selected to convert a tetragonal BSCCO 2212 oxide into an orthorhombic BSCCO 2212 oxide and, thereafter, roll worked in a high reduction draft in a range of about 40 % to 95 % in thickness so that the filaments have a constraining dimension is substantially equivalent to a longest dimension of the oxide superconductor grains. The rolled article is sintered to obtain a BSCCO 2223 oxide superconductor.</p> |