摘要 |
The invention provides a high strength steel sheet which exhibits excellent chemical convertibility and corrosion resistance after electrodeposition coating even in the case where the steel sheet has a high Si content, and a method for manufacturing such steel sheets. The method includes continuous annealing of a steel sheet which includes, in terms of mass%, C at 0.01 to 0.18%, Si at 0.4 to 2.0%, Mn at 1.0 to 3.0%, Al at 0.001 to 1.0%, P at 0.005 to 0.060% and S at <= 0.01%, the balance being represented by Fe and inevitable impurities, while controlling the dew-point temperature of the atmosphere to become not less than -10°C when the heating furnace inside temperature is in the range of not less than A°C and not more than B°C during the course of heating (A: 600 <= A <= 780, B: 800 <= B <= 900). |