发明名称 |
Method of manufacturing fabric with cool effect |
摘要 |
A method of manufacturing fabric includes adding 900 g of a material having a 92 wt % of SiO2 and 5 wt % of zinc oxide (ZnO) and 1,500 g of PU resin to water to mix until a first solution is formed; pouring the first solution into a first foaming tank; agitating the first solution in the first foaming tank to foam; adding a bridging agent and a foaming agent to a second foaming tank to mix with water to foam until a second solution is formed; pouring the first and second solutions into a third tank to mix and form a coating solution; continuously conveying a fabric sheet to a top of a platform; activating squeegees to spread the coating solution on the fabric sheet to form a cooling layer thereon; and performing a dry setting finish on the fabric sheet. |
申请公布号 |
US9469926(B2) |
申请公布日期 |
2016.10.18 |
申请号 |
US201314071868 |
申请日期 |
2013.11.05 |
申请人 |
GRAND TEXTILE CO., LTD. |
发明人 |
Lu Jen-Huan |
分类号 |
D06C7/02;D06M11/44;D06M11/79;D06M15/263;D06M15/564;D06M23/04;D06N3/00;D06N3/14 |
主分类号 |
D06C7/02 |
代理机构 |
|
代理人 |
|
主权项 |
1. A method of manufacturing fabric comprising the steps of:
adding 900 g of a material having a 92 wt % of silicon dioxide (SiO2) and 5 wt % of zinc oxide (ZnO) and 1,500 g of polyurethane (PU) resin to water to mix until a first solution of 30 liter is formed; pouring the first solution into a first foaming tank; agitating the first solution in the first foaming tank to foam; adding a bridging agent and a foaming agent to a second foaming tank to mix with water to foam until a second solution having a volume of 100 liter is formed; pouring the first and second solutions into a third tank to mix and form a coating solution; continuously conveying a fabric sheet to a top of a platform; activating a squeegee to spread the coating solution on the fabric sheet to form a cooling layer; and performing a dry setting finish on the fabric sheet coated with the cooling layers. |
地址 |
New Taipei TW |