There is provided a process for producing a precursor film for a polypropylene-based resin retardation film that can yield films with almost no orientation and with high transparency. The process for producing a precursor film for a polypropylene-based resin retardation film comprises a step of pressing a molten sheet formed by extruding a molten polypropylene-based resin from a T-shaped die 12 at 180° C. or higher and 300° C. or lower between a cooling roll 16 having a surface temperature regulated to −5° C. or higher and 30° C. or lower and a touch roll 14 having a surface temperature regulated to 80° C. or higher and 150° C. or lower, whereby the molten sheet is cooled and solidified. |