| 摘要 |
The present invention provides a polymer electrolyte fuel cell separator made of pure titanium or a titanium alloy superior in contact resistance with carbon paper and a method of production of the same, that is, a separator having a surface layer part to which conductive compound particles are affixed, characterized in that the surface oxide has a thickness of 3 to 15 nm in range, an average carbon concentration in a range from an outermost surface, including the oxide layer, to a depth of 100 nm is 0.02 to 6 at%, and the conductive compound particles have an average particle size of 0.01 to 20 µm. Further, the method of production of the present invention is characterized by forming, blast treating a surface of the formed article by particles comprised of conductive compound particles of an average particle size of 0.01 to 20 µm covering a surface of superhard core particles, impregnating it by a nitric acid aqueous solution of a concentration of 15 to 71 mass% and a temperature of 40 to 100°C for 30 seconds to 180 minutes by spraying or dipping, then washing it. |