COMPOSITE OXIDE PARTICLE HAVING BLACK COLOR

摘要

The complex oxide particles of the present invention are conductive and exhibit a black color. The particles contain cobalt in an amount of 40 to 65 % by mass in terms of the metal element based on the whole particles and at least one kind or two or more kinds of metals selected from copper, nickel and molybdenum. The particles are preferably prepared in the following manner: an aqueous solution of mixed metal salts prepared from water-soluble salts, wherein the aqueous solution contains cobalt and one kind or two or more kinds of metal element selected from copper, nickel and molybdenum, is mixed and neutralized with an alkali hydroxide to obtain a metal hydroxide slurry; the resultant slurry of metal hydroxides is kept at a pH of 10 to 13 and oxidized at a temperature of higher than 40°C and 60°C or less to obtain a precursor slurry; the resultant precursor slurry is aged at 80 to 150°C; and then, after solid-liquid separation, the resultant solid is heated at 400 to 700°C for longer than 1 hour and 3 hours or less.