CLEAR AND FLAME RETARDANT POLYCARBONATE RESIN FILM

摘要

The disclosure relates to a polycarbonate resin film with excellent clarity and flame retardance. The compositions comprise 100 parts by weight of a polycarbonate resin (A). The compositions further comprise 0.10 to 0.18 parts by weight of an alkali metal or alkaline earth metal salt compound (B) of a perfluoroalkane sulfonic acid. The compositions further comprise 0.05 to 0.35 parts by weight of a silicone compound (C). The film has an average thickness of 200 to 500 mum, a degree of haze of 5% or lower as measured according to the conditions specified in JIS K7105, and a flame retardance of VTM-1 or VTM-0 at a thickness of 300 mum as measured according to the UL94 test specified by the Underwriters Laboratories (UL).