STEEL SHEET FOR CAN AND METHOD FOR MANUFACTURING THE SAME |
摘要 |
A steel sheet exhibiting good drawability and excellent buckling strength of a can body portion against an external pressure, and a method for manufacturing the same. The steel sheet includes C: 0.0030% or more and 0.0100% or less, Si: 0.05% or less, Mn: 0.10% or more and 1.0% or less, P: 0.030% or less, S: 0.020% or less, Al: 0.010% or more and 0.100% or less, N: 0.0050% or less, Nb: 0.010% or more and 0.050% or less, and incidental impurities. Contents of C and Nb satisfy 0.10 ([Nb]/92.9)/([C]/12)<0.60, the HR30T hardness of the steel sheet is 56 or more, and the average Young's modulus of the steel sheet is 210 GPa or more. |
申请公布号 |
US2016160308(A1) |
申请公布日期 |
2016.06.09 |
申请号 |
US201414906131 |
申请日期 |
2014.07.08 |
申请人 |
JFE STEEL CORPORATION |
发明人 |
SAITO Hayato;NAKAGAWA Yusuke;KOJIMA Katsumi;NAKAMARU Hiroki |
分类号 |
C21D9/46;C21D6/00;C21D1/26;C22C38/00;C22C38/12;C22C38/06;C22C38/04;C22C38/02;C21D8/02;C22C38/14 |
主分类号 |
C21D9/46 |
代理机构 |
|
代理人 |
|
主权项 |
1. A steel sheet for a can, the steel sheet comprising:
C: 0.0030% or more and 0.0100% or less, by mass %; Si: 0.05% or less, by mass %: Mn: 0.10% or more and 1.0% or less, by mass %; P: 0.030% or less, by mass %; S: 0.020% or less, by mass % Al: 0.010% or more and 0.100% or less, by mass %; N: 0.0050% or less, by mass %; Nb: 0.010% or more and 0.050% or less, by mass %; and Fe and incidental impurities, wherein:
the contents of C and Nb satisfy Formula (1):
10≦([Nb]/92.9)/([C]/12)<0.60 Formula (1), [Nb] and [C] represent the contents (mass %) of Nb and C, respectively,
the steel sheet has a HR30T hardness of 56 or more, andthe steel sheet has an average Young's modulus of 210 GPa or more. |