| 摘要 |
An aluminum paste comprising particulate aluminum, an organic vehicle and glass frit selected from (i) lead-free glass frits with a softening point temperature in the range of 550 to 611° C. and containing 11 to 33 wt.-% of SiO2, >0 to 7 wt.-% of Al2O3 and 2 to 10 wt.-% of B2O3 and (ii) lead-containing glass frits with a softening point temperature in the range of 571 to 636° C. and containing 53 to 57 wt.-% of PbO, 25 to 29 wt.-% of SiO2, 2 to 6 wt.-% of Al2O3 and 6 to 9 wt.-% of B2O3, useful in the production of aluminum back electrodes of PERC silicon solar cells. |