发明名称 |
PREPARATION METHOD OF GRAPHENE/METAL COMPOSITE BOARD |
摘要 |
A method for preparing a graphene/metal composite sheet includes adding polyvinyl alcohol into distilled water and heat to about 100° C. under stirring to prepare a polyvinyl alcohol solution; dispersing graphene in distilled water using ultrasonication to prepare a graphene solution; mixing the polyvinyl alcohol solution and the graphene solution to form a graphene/polyvinyl alcohol mixed slurry; after a metal sheet is subjected to a surface activation treatment, coating the graphene/polyvinyl alcohol mixed slurry onto the metal sheet at both upper and lower surfaces; vacuum sintering to remove the polyvinyl alcohol in the surface coating to obtain a graphene/metal plate; overlaying at least two graphene/metal plates and bonding them together via hot isostatic pressing to form multilayer graphene/metal plates; and hot rolling the bonded multilayer graphene/metal plates to form the graphene/metal composite sheet. |
申请公布号 |
US2017015092(A1) |
申请公布日期 |
2017.01.19 |
申请号 |
US201615281790 |
申请日期 |
2016.09.30 |
申请人 |
AVIC BEIJING INSTITUTE OF AERONAUTICAL MATERIALS |
发明人 |
Yan Shaojiu;Yang Cheng;Hong Qihu;Liu Dabo;Dai Shenglong;Lin Zuoming |
分类号 |
B32B37/12;B32B7/12;B32B15/01;B05D3/02;B32B37/10;B32B38/00;B05D1/02;F41H5/04;B32B37/06 |
主分类号 |
B32B37/12 |
代理机构 |
|
代理人 |
|
主权项 |
1. A method for preparing a graphene/metal composite sheet, wherein: the method comprises:
adding polyvinyl alcohol into distilled water and heat to about 100° C. under stirring to prepare a polyvinyl alcohol solution; dispersing graphene in distilled water using ultrasonication to prepare a graphene solution; mixing the polyvinyl alcohol solution and the graphene solution to form a graphene/polyvinyl alcohol mixed slurry; after a metal sheet is subjected to a surface activation treatment, coating the graphene/polyvinyl alcohol mixed slurry onto the metal sheet at both upper and lower surfaces; vacuum sintering to remove the polyvinyl alcohol in the surface coating to obtain a graphene/metal plate; overlaying at least two graphene/metal plates and bonding them together via hot isostatic pressing to form multi layer graphene/metal plates; and hot rolling the bonded multilayer graphene/metal plates to form the graphene/metal composite sheet. |
地址 |
Beijing CN |