Method for producing sintered components by HIP |
摘要 |
The present invention relates to a method for manufacturing metal components comprising the following steps;
a. obtaining a metal powder composition comprising a particulate lubricant and a metal powder, wherein the metal powder particles have a size of less than 75µm, and the lubricant particles have a size of less than 25µm;
b. compacting said metal powder composition in a mould to a density of at least 7.3g/cm 3 to produce a green component;
c. sintering the green component at a temperature of at least 1300°C during at least 1 hr to produce a sintered component;
d. treating the sintered component without under a pressure of at least 900MPa during an elevation of the temperature to 1100°C; thereby obtaining a metal component having >99% of the theoretical density. |
申请公布号 |
EP3031550(A1) |
申请公布日期 |
2016.06.15 |
申请号 |
EP20140197265 |
申请日期 |
2014.12.11 |
申请人 |
HÖGANÄS AB (PUBL) |
发明人 |
MIEDZINSKI, ARTUR;FLODIN, ANDERS |
分类号 |
B22F1/00;B22F3/14;B22F3/15;B22F3/16 |
主分类号 |
B22F1/00 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|