A primary object of the present invention is to provide a method for continuous casting with which slabs for heavy gauge steel plate in which porosities are decreased can be manufactured. In the present invention, when a slab for heavy gauge steel plate is continuously cast, two pairs of reduction rolls that are arranged separately from each other with a roll-interval in a range from 3 m to 7 m, between which a support roll is arranged, are used, reduction is carried out on the slab by 3 to 15 mm with the reduction rolls at the first stage under the condition where the slab includes an unsolidified portion with the solid-phase ratio in a range from 0.8 to less than 1, and reduction is further carried out on the slab with the reduction rolls at the second stage under the condition where the slab is completely solidified. |