HIGH STRENGTH Cu-Ni-Co-Si BASED COPPER ALLOY SHEET MATERIAL AND METHOD FOR PRODUCING THE SAME, AND CURRENT CARRYING COMPONENT

摘要

A copper alloy sheet material comprises (by mass %) from 2.50 to 4.00% in total of Ni and Co, from 0.50 to 2.00% of Co, from 0.70 to 1.50% of Si, from 0 to 0.50% of Fe, from 0 to 0.10% of Mg, from 0 to 0.50% of Sn, from 0 to 0.15% of Zn, from 0 to 0.07% of B, from 0 to 0.10% of P, from 0 to 0.10% of REM, from 0 to 0.01% in total of Cr, Zr, Hf, Nb and S, the balance Cu and unavoidable impurities. A number density of coarse secondary phase particles (particle diameter of 5 mm or more) is 10 per mm2 or less. A number density of fine secondary phase particles (particle diameter of from 5 to 10 nm) is 1.0·109 per mm2 or more. A Si concentration in the parent phase is 0.10% by mass or more.

主权项

1. A copper alloy sheet material comprising a chemical composition containing from 2.50 to 4.00% in total of Ni and Co, from 0.50 to 2.00% of Co, from 0.70 to 1.50% of Si, from 0 to 0.50% of Fe, from 0 to 0.10% of Mg, from 0 to 0.50% of Sn, from 0 to 0.15% of Zn, from 0 to 0.07% of B, from 0 to 0.10% of P, from 0 to 0.10% of REM (rare earth elements), from 0 to 0.01% in total of Cr, Zr, Hf, Nb and S, the balance of Cu, and unavoidable impurities, all in terms of percentage by mass; containing secondary phase particles present in a parent phase, in which a number density of coarse secondary phase particles having a particle diameter of 5 μm or more is 10 per mm2 or less, and a number density of fine secondary phase particles having a particle diameter of from 5 to 10 nm is 1.0×109 per mm2 or more; and having an Si concentration in the parent phase of 0.10% by mass or more.