Method of environmentally friendly melting and refining of a glass melt for a crystallizable glass of a lithium aluminium silicate (LAS) glass ceramic

摘要

The method of environmentally friendly melting and refining a glass melt of a crystallizable glass, which is used for making a lithium aluminum silicate (LAS) glass ceramic, includes the steps of providing a glass batch with a main batch composition within a lithium aluminum silicate (LAS) glass system, in which 0.1-<0.6% by weight of tin oxide has been added as main refining agent, but which does not contain arsenic oxide and/or antimony oxide as refining agent, formulating a raw material mixture for the glass batch, so that less than 40% by weight of the raw material mixture is quartz sand and then refining a glass melt formed from the glass batch at temperatures of at least 1600° C.

主权项

1. A method of environmentally friendly melting a glass batch to form a glass melt of a crystallizable glass and of refining said glass melt of said crystallizable glass, said crystallizable glass being useful for making a lithium aluminium silicate (LAS) glass ceramic, said method consisting of the steps of:
a) providing a glass batch consisting of a raw material mixture, so that said glass batch has a main batch composition within a lithium aluminium silicate (LAS) glass system, in which a refining agent has been added, said refining agent consisting of 0.1-<0.6% by weight of tin oxide and 0.05-0.3% by weight of Fe2O3, said glass batch does not contain any arsenic oxide and does not contain any antimony oxide for refining, said raw material mixture comprises quartz sand and at least one member selected from the group consisting of petalite and spodumene, and said quartz sand is present in said raw material mixture in an amount of less than 40 wt. %; b) melting said glass batch in a melting tank to form a glass melt; c) refining said glass melt with oxygen produced from said main refining agent at temperatures of at least 1600° C. in said melting tank; and d) choosing a throughput of said glass melt through said melting tank or an average residence time of the glass melt in the melting tank so that a bubble count of bubbles with a size of at least 100 μm below 1 bubble per kg; wherein said glass batch substantially consists, in % by weight based on oxide content, of:Li2O3.0-4.2Σ Na2O + K2O0.2-1.5MgO  0-1.5Σ CaO + SrO + BaO0-4ZnO0-2B2O30-2Al2O319-23SiO260-69TiO22.5-4  ZrO20.5-2  P2O50-3SnO2 0.1-<0.6Σ TiO2 + ZrO2 + SnO23.8-6  V2O50.01-0.06Fe2O30.05-0.3; so that a colored glass ceramic with a beta-quartz solid solution as predominant crystal phase can be formed from the crystallizable glass after said refining.