发明名称 |
METHOD OF MANUFACTURING MICROENCAPSULATED PHASE-CHANGE MATERIAL-CONTAINING GYPSUM PLATE CAPABLE OF FLAME RETARDATION AND TEMPERATURE VARIATION ATTENUATION |
摘要 |
A method of manufacturing a microencapsulated phase-change material-containing gypsum plate capable of flame retardation and temperature variation attenuation is introduced, such that an organic microencapsulated phase-change material is uniformly distributed in an inorganic gypsum plate. The method involves putting a microencapsulated phase-change material in a dispersing agent solution, blending the dispersing agent solution to form a first solution, putting the foaming agent in the first solution, putting gypsum powder and starch in the first solution, blending the first solution to form a microencapsulated phase-change material gypsum mixture solution, molding the microencapsulated phase-change material gypsum mixture solution to finalize the manufacturing of a microencapsulated phase-change material-containing gypsum plate capable of flame retardation and temperature variation attenuation. Due to the microencapsulated phase-change material, dispersing agent, and foaming agent, gas generated from the microencapsulated phase-change material heated at high temperature is quickly discharged from the gypsum plate without destructing original structure thereof. |
申请公布号 |
US2015329783(A1) |
申请公布日期 |
2015.11.19 |
申请号 |
US201414279362 |
申请日期 |
2014.05.16 |
申请人 |
NATIONAL CHUNG SHAN INSTITUTE OF SCIENCE AND TECHNOLOGY |
发明人 |
TSAI PING-SZU;YU YI-HSIUAN;HSIEH JENG-PEI;LEE SHU-HUA;HSIEH HOU-AN |
分类号 |
C09K21/14;B29C44/34;B29C44/02;E04B1/78 |
主分类号 |
C09K21/14 |
代理机构 |
|
代理人 |
|
主权项 |
1. A method of manufacturing a microencapsulated phase-change material-containing gypsum plate capable of flame retardation and temperature variation attenuation, the method comprising the steps of:
A. providing a foaming agent aqueous solution; B. putting a microencapsulated phase-change material in the foaming agent aqueous solution, followed by performing thereon a first blending dispersing process to form a first solution, wherein the microencapsulated phase-change material and the foaming agent aqueous solution are immiscible; C. providing gypsum powder and starch, followed by performing a second blending dispersing process to form a second solution; D. putting the second solution in the first solution, followed by performing a third blending dispersing process to form a microencapsulated phase-change material gypsum mixture solution; and E. molding the microencapsulated phase-change material gypsum mixture solution to form a microencapsulated phase-change material-containing gypsum plate capable of flame retardation and temperature variation attenuation. |