| 摘要 |
<p>A high-strength, high-workability tin mill black plate contains 0.070% to less than 0.080% C, 0.003% to 0.10% Si, 0.51% to 0.60% Mn, and the like on a mass basis and has a tensile strength of 500 MPa or more and a yield elongation of 10% or more. The average size and the elongation rate of crystal grains are 5 µm or more and 2.0 or less, respectively, in cross section in the rolling direction thereof. The hardness difference obtained by subtracting the average Vickers hardness of a cross section ranging from a surface to a depth equal to one-eighth of the thickness of the plate from the average Vickers hardness of a cross section ranging from a depth equal to three-eighths of the plate thickness to a depth equal to four-eighths of the plate thickness is 10 points or more and/or the maximum Vickers hardness difference is 20 points or more. The high-strength, high-workability tin mill black plate is a material suitable for easy-open cans.</p> |