| 摘要 |
The present invention relates to a method for manufacturing a ceramic ware, wherein fluidity is provided to ceramic powder, which is a ceramic material, and the ceramic powder is molded and manufactured to a ceramic ware by using an injection mold. The method for manufacturing a ceramic ware according to the present invention comprises the steps of: mixing 60 to 75 wt% of ceramic powder, 25 to 40 wt% of a polyethylene glycol and a polypropylene resin and then heating and stirring at a temperature of 180-250 deg. C and thereby manufacturing a ceramic compound in a paste state; drying a ceramic compound in a paste state and crushing; heating the crushed ceramic compound by using a mold apparatus and melting a resin and then molding by injecting to a mold; immersing the molded ceramic ware in water and thereby removing a polyethylene glycol resin and then placing into a furnace and thereby removing a polypropylene resin; and coating a glaze on a surface of a ceramic ware from which a resin has been removed and then firing the same. |