The coil spring includes steel wire material containing 0.45 to 0.80 weight % of C, 0.15 to 2.50 weight % of Si, 0.3 to 1.0 weight % of Mn and iron and inevitable impurities as the remainder, and having a circle equivalent diameter of 2.5 mm to 10 mm, in which internal hardness at a freely selected cross section of the wire material is in a range of 570 to 700 Hv, C-condensed layer which exceeds average concentration of C contained in the steel wire material exists at surface layer part, and in an approximate maximum principal stress direction generated when a compressive load is loaded on spring of inner diameter side of the coil spring of the wire material, unloaded compressive residual stress at a depth of 0.2 mm and 0.4 min from surface of the wire material is not less than 200 MPa and not less than 60 MPa, respectively. |