| 摘要 |
Disclosed is a fluorine-containing elastomer having a copolymerization composition containing (A) 72.8 to 74.0 mol% of tetrafluoroethylene, (B) 26.8 to 24.0 mol% of perfluoro(lower alkyl vinyl ether) or perfluoro(lower alkoxy-lower alkyl vinyl ether), and (C) 0.2 to 3.0 mol% of a perfluoro unsaturated nitrile compound, and having a Mooney viscosity ML 1+10 (121°C) of 70 to 115. The fluorine-containing elastomer is compounded with a bisamidoxime compound, which is used as a vulcanizing agent, in an amount of 0.2 to 5 parts by weight based on 100 parts by weight of the fluorine-containing elastomer to form a fluorine-containing elastomer composition. The vulcanizate of the composition, even when used under plasma irradiation conditions or at temperatures as high as 300°C, can prevent weight loss caused by plasma irradiation and exhibits excellent heat resistance at temperatures as high as 300°C or more. |