Method for producing aligned carbon nanotube aggregate |
摘要 |
A production method in accordance with the present invention includes the steps of: providing a catalyst support layer by applying, to a substrate, a catalyst support layer coating agent obtained by dissolving in an organic solvent (i) an organometallic compound containing aluminum and/or a metal salt containing aluminum and (ii) a stabilizer for inhibiting a condensation polymerization reaction of the organometallic compound and/or the metal salt; providing a catalyst formation layer by applying, to the catalyst support layer, a catalyst formation layer coating agent obtained by dissolving in an organic solvent (a) an organometallic compound containing iron and/or a metal salt containing iron and (b) a stabilizer for inhibiting a condensation polymerization reaction of the organometallic compound and/or the metal salt; and growing an aligned carbon nanotube aggregate on the substrate by chemical vapor deposition (CVD). |
申请公布号 |
US9045344(B2) |
申请公布日期 |
2015.06.02 |
申请号 |
US201113581812 |
申请日期 |
2011.02.28 |
申请人 |
ZEON CORPORATION;NATIONAL INSTITUTE OF ADVANCED INDUSTRIAL SCIENCE AND TECHNOLOGY |
发明人 |
Takai Hirokazu;Uejima Mitsugu;Hoang The Ban;Hata Kenji;Yumura Motoo |
分类号 |
D01F9/12;B82Y40/00;C01B31/02;B01J23/745;B01J37/02;B82Y30/00 |
主分类号 |
D01F9/12 |
代理机构 |
Birch, Stewart, Kolasch & Birch, LLP |
代理人 |
Birch, Stewart, Kolasch & Birch, LLP |
主权项 |
1. A method of producing an aligned carbon nanotube aggregate, comprising the steps of:
dissolving in an organic solvent (i) an organometallic compound containing aluminum and/or a metal salt containing aluminum and (ii) a stabilizer for inhibiting a condensation polymerization reaction of the organometallic compound and the metal salt to obtain a catalyst support layer coating agent; applying the catalyst support layer coating agent to a substrate; heating the catalyst support layer coating agent to obtain a catalyst support layer on the substrate; dissolving in an organic solvent (a) an organometallic compound containing iron and/or a metal salt containing iron and (b) a stabilizer for inhibiting a condensation polymerization reaction of the organometallic compound and the metal salt to obtain a catalyst formation layer coating agent; applying the catalyst formation layer coating agent to the catalyst support layer; heating the catalyst formation layer coating agent to obtain a catalyst formation layer on the catalyst support layer; and growing an aligned carbon nanotube aggregate on the substrate by chemical vapor deposition (CVD). |