Aluminum alloy material for forging

摘要

An aluminum alloy forging material of the present invention is constituted by an aluminum alloy cast product obtained by subjecting an aluminum alloy ingot having a structure in which a secondary dentrite arm spacing (DAS) is 40 μm or less and an average grain diameter of crystallized substances is 8 μm or less to homogenization treatment for holding the ingot for one hour or more under temperature conditions of 450 to 510° C., wherein the ingot is obtained by continuously casting a molten aluminum alloy having an alloy composition consisting of: Si: 0.80 to 1.15 mass %; Fe: 0.2 to 0.5 mass %; Cu: 3.8 to 5 mass %; Mn: 0.8 to 1.15 mass %; Mg: 0.5 to 0.8 mass %; Zr: 0.05 to 0.13 mass %; and Ti contained in such an amount that a sum of Ti and Zr is 0.2 mass % or less, and the balance being Al and inevitable impurities, wherein the alloy composition satisfies a Cu/Mg ratio of 8 or less, Ti is added in a form of an Al master alloy (5Ti-1B mother alloy) in which Ti and B are contained at a ratio of 5:1, and a Ti/Zr ratio satisfies 0.3 or higher.

主权项

1. A method of manufacturing an aluminum alloy forging material, comprising:
obtaining an aluminum alloy ingot having a structure in which a secondary dentrite arm spacing (DAS) is 40 μm or less and an average grain diameter of crystallized substances is 8 μm or less by continuously casting a molten aluminum alloy having an aluminum composition consisting of: Si: 0.80 to 1.15 mass %; Fe: 0.2 to 0.5 mass %; Cu: 3.8 to 5 mass %; Mn: 0.8 to 1.15 mass %; Mg: 0.5 to 0.8 mass %; Zr: 0.05 to 0.13 mass %; and Ti contained in such an amount that a sum of Ti and Zr is 0.2 mass % or less, and the balance being Al and inevitable impurities, wherein the alloy composition satisfies a Cu/Mg ratio of 8 or less, Ti is added in a form of a 5Ti-1B mother alloy, and Ti/Zr ratio satisfies 0.3 or higher; obtaining an aluminum alloy cast product by subjecting the aluminum alloy ingot to homogenization treatment for holding the product for one hour or more at temperatures of 450 to 510° C., hot forging the aluminum alloy cast product under temperature conditions of 400 to 510° C., subjecting the aluminum alloy cast product to a solution treatment under temperature conditions of 450 to 510° C., and subjecting the aluminum alloy cast product to an aging treatment, wherein the aluminum alloy cast product is constituted as the aluminum alloy forging material.