| 摘要 |
A multifunctional BOPP cigarette packaging film comprises an upper layer (1), a middle-upper layer (2), a middle layer (3), a middle-lower layer (4) and a lower layer (5). The upper layer (1) is a binary copolymerized polypropylene surface layer, both the middle-upper layer (2) and the middle-lower layer (4) are homopolymerized polypropylene antibacterial agent layers, the middle layer (3) is a homopolymerized polypropylene stiffening agent layer, the lower layer (5) is a binary copolymerized polypropylene bottom surface layer. Also disclosed is a manufacturing method for the multifunctional BOPP cigarette packaging film. The packaging film acts as an effective barrier, has slip property and relatively low moisture permeability as well as low cost, and is suitable for a high-speed packing machine. |
| 主权项 |
1. A manufacturing method for a multifunctional BOPP cigarette packaging film which is characterized in that: said manufacturing method comprises the following steps:
(1) selecting materials: in the multifunctional BOPP cigarette packaging film, the upper layer is a binary copolymerized polypropylene surface layer, the middle-upper layer and the middle-lower layer are homopolymerized polypropylene antibacterial agent layers, the middle layer is a homopolymerized polypropylene stiffening agent layer, and the lower layer is a binary copolymerized polypropylene bottom surface layer; the upper layer accounts for 8 to 15 percent of the total mass, the middle-upper layer accounts for 12 to 21 percent of the total mass, the middle layer accounts for 38 to 50 percent of the total mass, the middle-lower layer accounts for 12 to 21 percent of the total mass, and the lower layer accounts for 8 to 15 percent of the total mass; the binary copolymerized polypropylene surface layer and the binary copolymerized polypropylene bottom surface layer respectively comprise the following three components in parts by mass: 7 to 11 parts of binary copolymerized polypropylene, 0.5 to 3.5 parts of thermoplastic elastomer, and 0.5 to 3.5 parts of super-slip/anti-blocking master batch; the homopolymerized polypropylene antibacterial agent layer comprises the following three components in parts by mass: 11 to 14 parts of homopolymerized polypropylene (PP), 0.5 to 3.5 parts of antibacterial master batch, and 0.5 to 3.5 parts of rapid migration antistatic master batch; the homopolymerized polypropylene stiffening agent layer comprises the following three components in parts by mass: 25.5 to 32.5 parts of homopolymerized polypropylene (PP), 0.5 to 4.5 parts of antistatic/slip master batch, and 5 to 20 parts of special stiffening master batch; (2) manufacturing the film: a co-extrusion biaxial orienting method is adopted, comprising the following processes: (2.1) feeding prepared mixtures into five extruders through a feeder, wherein the five extruders respectively correspond to the upper layer, the middle-upper layer, the middle layer, the middle-lower layer and the lower layer; extruding in a molten state, filtering for multiple times through a filter, feeding the filtrate into a T-shaped die head, and extruding the melt through a die lip; (2.2) tape-casting: tightly attaching the melt extruded from the die lip to the surface of a quenching roller, and forming a cast film under the actions of the quenching roller, a water bath and a guide roller; (2.4) orienting: leading out the cast film, and performing longitudinal orienting and then transverse orienting; (2.5) cooling and forming; (2.6) traction winding-up: winding the film into a cylindrical film roll by edge cutting, thickness measuring and corona treatment, and thus obtaining the multifunctional BOPP cigarette packaging film. |