| 摘要 |
A solder powder having an average particle diameter of, for example, 0.05 µm or more and less than 3 µm is obtained by a method of producing a solder powder, including the steps of: putting solid or liquid metal, a non-aqueous solvent, and crushing balls having a diameter of 0.05 mm to 5 mm into a container to obtain a mixture; heating the mixture to 150°C or higher and stirring the mixture; separating the crushing balls from the mixture after the stirring to obtain a mixture of the solder powder and the non-aqueous solvent; and performing solid-liquid separation on the mixture of the solder powder and the non-aqueous solvent to obtain a solder powder. |