PHOTOSTABLE COMPOSITE FOR SOLAR WATER SPLITTING AND PROCESS FOR THE PREPARATION THEREOF

摘要

The present invention discloses photostable composite of indium gallium nitride and zinc oxide for solar water splitting, comprising Indium content in the range of 1-40 wt %, Ga content in the range of 1 to 15 wt %, nitrogen content in the range of 0.1 to 5 wt %, and the remaining is ZnO. The combusiton synthesis comprises the steps of: (a) dissolving 45 to 55 wt % urea, 75 to 80 wt % Zinc nitrate, 3 to 5 wt % Gallium nitrate, and 15 to 20 wt % Indium nitrate in water with stirring until a homogenous solution is formed; and (b) heating the homogenous solution of step (a) at a temperature in the range of 450-550 [deg.]C for period in the range of 2 to 20 min to obtain the photostable composite. '