PROCESS OF MELT-SPINNING POLYACRYLONITRILE FIBER

摘要

Processes for producing carbon fibre, the filament thereof and pre-oxidized fibre are provided. In one embodiment, the gel spinning of polyacrylonitrile filament is achieved by using small-molecule gelling agent, and the carbon fibre obtained thereby is increased by 15% to 40% in tensile strength and by 20% to 35% in toughness. In another embodiment, the melt spinning process of polyacrylonitrile is conducted by using imidazole type ion liquid as plasticizer, the process reduces environment pollution, is suitable for industrial production and the fibre produced thereby is improved in its strength. In yet another embodiment, polyacrylonitrile pre-oxidized fibre is produced by melt spinning, so low cost and controllable pre-oxidization of polyacrylonitrile can be achieved. In a further embodiment, high strength carbon fibre is manufactured by using polymer thickening agent. In another further embodiment, low cost and controllable pre-oxidization of polyacrylonitrile is achieved by conducting pre-oxidization before spinning, minimizing skin-core structure, so as to produce high performance carbon fibre, and reduce the production cost of carbon fibre greatly.

主权项

1. A melt spinning process for producing a PAN-based pre-oxidized fibre, comprising the following steps:
a) dissolving a catalyst for pre-oxidation of PAN in an ionic liquid in a weight ratio from 1:100 to 0.01:100 followed by adding PAN powder to obtain a mixture, wherein the weight ratio of PAN powder to ionic liquid is between 1:1 and 1:0.25; b) adding the mixture from step a) to a hopper of twin-screw spinning machine to conduct melting spinning while blowing an oxygen-containing gas into a melting segment of the twin-screw spinning machine, wherein the flow rate of the oxygen-containing gas is between 1 ml/min and 5 ml/min, and the rotational velocity of screw is between 40 and 120 r/min, and the temperature at a feed segment is between 170° C. and 185° C., and the temperature for plasticizing is between 185° C. and 220° C., and the temperature for melting is between 185° C. and 220° C.; c) dry-heat drawing the spun fibre directly under a temperature between 110 and 140° C. with a total draw ratio between 4 and 6, then washing the drawn fibre with water at 70-90° C., followed by thermosetting in dry hot air at 120-150° C. to give the PAN based pre-oxidized fibre.