Manufacturing method for glass base material

摘要

Provided is a method for manufacturing glass preforms with high yield. In the glass-preform manufacturing method according to the present invention, a glass preform is produced through a fixing step, a deposition step, an extraction step, a vitrification step, and a collapsing step in the enumerated order. At the deposition step, the mean density of the glass soot body deposited on the circumference of the tubular handle 12 is made higher than the mean density of the glass soot body deposited on the circumference of the starting mandrel 11. It is preferable that the longitudinal variation in the mean density of a glass soot body deposited from the start of deposition to the tenth layer of glass particles within the range of ±50 mm from the boundary position between the starting mandrel and the tubular handle be 0.01 g/cc/mm or less.

主权项

1. A method of manufacturing a glass preform, comprising:
a fixing step for preparing a starting member by inserting a starting mandrel into a tubular handle and fixing such that the tip portion of the starting mandrel protrudes from an end of the tubular handle; a deposition step for producing a glass soot body by depositing glass particles on the circumference of the starting member by subjecting the starting member and a glass synthesizing burner to relative two-way motions along the starting mandrel in a range extending from the tip portion of the starting mandrel to a part of the tubular handle; an extraction step for pulling out the starting mandrel from the tubular handle and the glass soot body; a vitrification step for producing a consolidated glass pipe by heating the glass soot body after the extraction step; and a collapsing step for making a solid glass preform by reducing a pressure inside of the consolidated glass pipe and heating the consolidated glass pipe, wherein the mean density of a glass soot body deposited on the circumference of the tubular handle is made larger than the mean density of a glass soot body deposited on the circumference of the starting mandrel, and the longitudinal variation in the mean density of a glass soot body deposited from the start of deposition to the tenth layer of glass particles within the range of ±50 mm from the end of the tubular handle is 0.01 g/cc/mm or less.