Silica container and method for producing the same

摘要

A method for producing a silica container includes forming a preliminarily molded substrate, wherein a first powdered raw material is fed to an inner wall of an outer frame having aspiration holes while rotating the outer frame; forming a preliminarily molded intermediate layer, wherein a second powdered raw material added with an aluminum compound or a crystal nucleating agent as an additive is fed to an inner wall of the preliminarily molded substrate; and forming an inner layer, wherein the preliminarily molded substrate and the preliminarily molded intermediate layer are degassed by aspiration from a peripheral side with heating from an inside forming a substrate and an intermediate layer, and a third powdered raw material having a high silica purity is spread from inside the substrate having the formed intermediate layer with heating from the inside forming an inner layer on an inner surface of the intermediate layer.

主权项

1. A method for producing a silica container comprising at least a substrate comprised of a silica as its main component and having a rotational symmetry, an intermediate layer formed on an inner wall of the substrate, and an inner layer formed on an inner wall of the intermediate layer, wherein the method comprises:
a step of preparing a first powdered raw material comprising silica particles, for forming the substrate, a step of adding, as an additive, at least any one of an aluminum compound and a powdered compound capable of becoming a crystal nucleating agent for crystallization of a silica glass, into a second powdered raw material comprising silica particles, for forming the intermediate layer, a step of forming a preliminarily molded substrate, wherein the first powdered raw material is fed to an inner wall of an outer frame having a rotational symmetry and aspiration holes arranged in the inner wall while rotating the outer frame thereby preliminarily molding to an intended shape in accordance with the inner wall of the outer frame, a step of forming a preliminarily molded intermediate layer, wherein the second powdered raw material added with the additive is fed to an inner wall of the preliminarily molded substrate thereby preliminarily molding to an intended shape in accordance with the inner wall of the preliminarily molded substrate, a step of forming the substrate and the intermediate layer, wherein the preliminarily molded substrate and the preliminarily molded intermediate layer are degassed by aspiration from an outer side of the preliminarily molded substrate through the aspiration holes formed in the outer frame and at the same time heated from inside the preliminarily molded substrate and the preliminarily molded intermediate layer by a discharge-heat melting method thereby forming an outer part of the preliminarily molded substrate into a sintered body constituting an outer portion of the substrate while forming an inner part of the preliminarily molded substrate into a fused glass body constituting an inner portion of the substrate, and forming the preliminarily molded intermediate layer into a fused glass body constituting the intermediate layer, and a step of forming the inner layer on an inner surface of the intermediate layer, wherein a third powdered raw material comprised of a crystalline silica and having a higher silica purity than the first powdered raw material is spread from inside the substrate on which the intermediate layer was formed and at the same time heated from the inside by a discharge-heat melting method.