| 摘要 |
<p>The present invention aims to provide a titanium oxide paste which is excellent in printability and which allows for production of a porous titanium oxide layer having a high porosity with a small amount of impurities on the surface thereof even by low-temperature firing, a method of producing a porous titanium oxide laminate using the titanium oxide paste, and a dye-sensitized solar cell. The titanium oxide paste of the present invention contains titanium oxide particles, a (meth)acrylic resin, and an organic solvent. The paste has a viscosity of 15 to 50 Pa·s and a thixotropic ratio of 2 or greater. A dried mass obtained by heating the paste at a temperature-increasing rate of 10°C/min from 25°C to 300°C in the atmospheric environment contains 1% by weight or less of the (meth)acrylic resin and the organic solvent.</p> |