| 摘要 |
<p>The present invention discloses a method of manufacturing a porcelain body having sintering flower, the method including: a mixing step of mixing 50 to 70 wt% of pink kaolin, 10 to 30 wt% of Obu clay, and 10 to 30 wt% of Milyang clay to prepare a porcelain body composition; a forming step of forming a green body with the porcelain body composition, and shaping a slip layer on the surface of the green body; a drying step of naturally drying the green body; a glazing step of glazing the surface of the dried green body with transparent emulsion which uses wood ash as a flux; and a firing step of firing the glazed green body in an oxidizing atmosphere at a firing temperature of 1,150 to 1,180°C to manufacture the porcelain body.</p> |