| 摘要 |
<p>A high strength galvanized steel sheet having excellent formability, weldability, and fatigue properties and a tensile strength equal to or higher than 980 MPa and a method for manufacturing the same. The steel sheet contains all in mass%, C: 0.05% to <0.12%, Si: 0.35% to <0.80%, Mn: 2.0 to 3.5%, P: 0.001 to 0.040%, S: 0.0001 to 0.0050%, Al: 0.005 to 0.1%, N: 0.0001 to 0.0060%, Cr: 0.01% to 0.5%, Ti: 0.010 to 0.080%, Nb: 0.010 to 0.080%, and B: 0.0001 to 0.0030%, optionally one or more of Mo: 0.01 to 0.15%, Ca: 0.0001 to 0.0050%, REM: 0.0001 to 0.1%, and Sb: 0.0001 to 0.1%, and Fe and unavoidable impurities as the balance, has a microstructure containing a ferrite phase with a volume fraction in a range of 20 to 70% and an average grain diameter equal to or smaller than 5 µm, and has a galvanized layer on a surface thereof at a coating weight (per side) of 20 to 150 g/m2.</p> |