摘要 |
A dielectric ceramic composition includes a component represented by composition formula {α(xBaO.yNd2O3.zTiO2)+β(2MgO.SO2)} as a main component and zinc oxide, boron oxide, and a glass having a softening point equal to or lower than a certain temperature as minor components with respect to the main component. In the dielectric ceramic composition, x, y, and z that respectively represent molar ratios of BaO, Nd2O3, and TiO2 are in certain ranges and α and β that represent volume ratios of subcomponents (xBaO.yNd2O3.zTiO2 and 2MgO.SiO2) in the main component are in certain ranges. When the minor components are respectively represented by aZnO, bB2O3, and cglass, a, b, and c that represent mass ratios of the respective minor components to the main component are in certain ranges. |
主权项 |
1. A dielectric ceramic composition comprising:
a component represented by composition formula {α(xBaO.yNd2O3.zTiO2)+β(2MgO.SiO2)} as a main component; and zinc oxide, boron oxide, and a glass having a softening point of 570° C. or less as minor components with respect to the main component, wherein x, y, and z that respectively represent molar ratios of BaO, Nd2O3, and TiO2 satisfy
14 (mol %)≦x≦19 (mol %),12 (mol %)≦y≦17 (mol %),65 (mol %)≦z≦71 (mol %), andx+y+z=100; α and β that represent volume ratios of subcomponents in the main component satisfy
35 (vol %)≦α≦65 (vol %),35 (vol %)≦β≦65 (vol %), andα+β=100; and when the minor components are respectively represented by aZnO, bB2O3, and cglass, a, b, and c that represent mass ratios of the respective minor components to the main component satisfy
0.0 (mass %)≦a≦4.25 (mass %),0.0 (mass %)≦b≦5.5 (mass %),4.5 (mass %)≦c≦10.0 (mass %),b≧a−3, anda+b+c=10. |