| 摘要 |
A nickel-based alloy comprises 9.5-14 wt.%, preferably 12 wt.% chromium, 7-11 wt.%, preferably 9 wt.% cobalt, 1-2.5 wt.%, preferably 1.85 wt.% molybdenum, 1.85%, 3-6 wt.%, preferably 3.7 wt.% tungsten, 0.5-2 wt.%, preferably 1 wt.% hafnium, 4.7-5.7 wt.%, preferably 5.2 wt.% tantalum, 2.9-4.4 wt.%, preferably 3.4 wt.% aluminum, 3.4-4.9 wt.%, preferably 3.9 wt.% titanium, 0.05-0.11 wt.%, preferably 0.09 wt.% carbon, 0.0175-0.003 wt.%, preferably 0.014 wt.% boron, 75 ppm to 1 wt.%, preferably 0.1 wt.% zirconium, 0.05+- 0.02 wt.% cerium, 0.05+- 0.02 wt.% lanthanum, and 1 wt.% or less niobium. A nickel-based alloy comprises 9.5-14 wt.%, preferably 12 wt.% chromium, 7-11 wt.%, preferably 9 wt.% cobalt, 1-2.5 wt.%, preferably 1.85 wt.% molybdenum, 1.85%, 3-6 wt.%, preferably 3.7 wt.% tungsten, 0.5-2 wt.%, preferably 1 wt.% hafnium, 4.7-5.7 wt.%, preferably 5.2 wt.% tantalum, 2.9-4.4 wt.%, preferably 3.4 wt.% aluminum, 3.4-4.9 wt.%, preferably 3.9 wt.% titanium, 0.05-0.11 wt.%, preferably 0.09 wt.% carbon, 0.0175-0.003 wt.%, preferably 0.014 wt.% boron, 75 ppm to 1 wt.%, preferably 0.1 wt.% zirconium, 0.05+- 0.02 wt.%, preferably 0.05 wt.% cerium, 0.05+- 0.02 wt.%, preferably 0.05 wt.% lanthanum, and 1 wt.% or less niobium. Independent claims are included for the following: (1) method for welding nickel-based substrate or cobalt-based substrate; and (2) welded component. |