Glasses having low softening temperatures and high toughness |
摘要 |
Glasses having a low softening point and high toughness. The glasses are alkali aluminoborosilicate glasses having softening points of less than 900° C. and, in some embodiments, in a range from about 650° C. up to about 825° C., and an indenter damage threshold of at least 300 g for glasses that are not chemically strengthened. The glasses are free of alkaline earth metals, lead, arsenic, antimony, and, in some embodiments, lithium. |
申请公布号 |
US8778820(B2) |
申请公布日期 |
2014.07.15 |
申请号 |
US201012788559 |
申请日期 |
2010.05.27 |
申请人 |
Corning Incorporated |
发明人 |
Gomez Sinue;Lamberson Lisa Ann;Morena Robert Michael |
分类号 |
C03C3/091;C03C3/083 |
主分类号 |
C03C3/091 |
代理机构 |
|
代理人 |
Santandrea Robert P. |
主权项 |
1. An alkali aluminoborosilicate glass, the glass having a softening point in a range from 650° C. up to 725° C. and an indenter damage threshold of at least 300 g, and wherein the glass has a B2O3/Al2O3 molar ratio of greater than 1.2 and is free of alkaline earth metals, lead, arsenic, and antimony. |